• Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks
  • Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks
  • Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks
  • Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks
  • Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks
  • Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks

Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks

Refractoriness (℃): 1770< Refractoriness< 2000
Feature: Long Time Materials, Instant Materials
Type: Refractory Material
Shape: Brick
Material: Silicon Carbide (SiC)
Sio2 Content: >23%
Samples:
US$ 0/Ton 1 Ton(Min.Order)
| Request Sample
Customization:
Diamond Member Since 2022

Suppliers with verified business licenses

Manufacturer/Factory

Basic Info.

Model NO.
TKSB04
Al2O3 Content (%)
>60
MGO Content (%)
0.2
Refractoriness (Degree)
1580< Refractoriness< 1770
Cro Content (%)
0.1~0.3%
Standard Size
230*114*65mm
Application
Coke Oven Repair,Glass Furnace
Fe2o3 %
1.0
Apparent Porosity %
20
Bulk Density g/cm3
2.6
Permanent Linear Change %
0~+0.2
Transport Package
Standard One
Specification
STANDARD ONE
Trademark
TK BRICKS
Origin
China
HS Code
69022000
Production Capacity
3000 Tons Per Month

Product Description

Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks
Silica brick is with high refractoriness and mechanical behavior under high temperature.
It is the necessary material of high- temperature service, mainly use for coke oven and glass furnace.

Items Silica Brick Silica Brick
Coke Oven Glass Furance
Al2O3 % ≤1.5 ≤0.5
Fe2O3 % ≤1.5  ≤0.8
SiO2 % ≥94.5 ≥96
K2O+Na2O % CaO≤2.5 CaO≤2.5
Refractoriness R ºC ≥1650 ≥1650
Refractoriness under Load KD ºC KD≥1650 KD≥1650
Permanent Linear Change % (1450ºC×2h) 0~+0.2 0~+0.2
Apparent Porosity % ≤22 ≤24 ≤21
Bulk density g/cm3 ≤2.33 ≤2.34  ≤2.34
Cold crushing strength Mpa  ≥40 ≥35 ≥35
0.2MPa creep rate % Residue Quartz ≤1.0% ≤1.0%
Thermal Expansivity(1000ºC) ≤1.28 ≤1.30 /
Application Bottom and Wall Regenerator Bottom and Wall Glass Furance


Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory BricksKiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory BricksKiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks

Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks Kiln Use Refractory Fire Bricks Silicon Carbide 1800 Degree Refractory Brick High Quality Silica Refractory Bricks

Send your message to this supplier

*From:
*To:
avatar Mr. Bill Yang
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now