Silicon Carbide Kiln Shelves / Sic Ceramic Fish Setters Plates 340X190mm

• Refractoriness (℃): Refractoriness> 2000
• Feature: Long Time Materials, Instant Materials
• Type: Refractory Material
• Shape: Plate
• Material: Sic
• Sio2 Content: Above 85%
• MGO Content: 0.2-1.3%
• Application: Refractory Furnace Lining Insulation Materials
• Density (Kg/M³ ): 2.2-3.15g/cm3
• Feature 1: Low Thermal Conductivity,Low Heat Storage
• Feature 2: Good Thermal Shock Resistance
• Feature 3: Reasonable Price
• Transport Package: Standard One
• Specification: Customized
• Trademark: TK BRICKS
• Origin: China
• HS Code: 381600000
• Production Capacity: 3000000 PCS Per Month

Product Description

Silicon carbide kiln shelves / SIC ceramic fish setters plates 340x190mm
 
Silicon Carbide kiln shelve is made of high quality synthetically made silicon carbide grains (SIC)  Containing SiC72% to 99%.
And selected bonding components, including oxidation bonded, Si3N4 bonded ,Sialon bonded , clay bonded etc.
The product has a high temperature, high strength, volume stability and good thermal conductivity, acid,
alkali and a variety of molten metal erosion ability and so on. widely used in colored aluminum tank, zinc vertical tank;
metallurgical industry, blast furnace lining, ceramic kiln shelf panels,

Features:
1. High temperature resistant
2. Various sizes available
3. Competitive prices
4. Small tolorence: +-0.005mm
5. Good quality
6. Exact delivery time

Item	RbSIC	SiSIC
Purity(%)	> 98	>90
Density(g/cm3 )	3.1-3.2	>3.05
Granularity(um)	0.5-0.7	8--20
Hardness(HRA)	≥90	≥90
Bending strength(MPa)	400-580	350-450
Compressive strength (MPa)	3900	>2500
Fracture strength (MPa)	3.05-4.6	4.3
Modulus of elasticity(GPa)	380-410	420
Thermal comductivity	102.6	35-110
Coefficient of thermal expansion(1/ºC)	4.02×10-6	4.3×10-6
Poisson's ratio	0.14	0.15
Open porosity (%)	7--8	<0.1
Temperature of application (ºC)	1800	1410

Item	SSIC
SIC Purity(%)	>98
Bulk Density(g/cm3 )	3.06-3.15
Max. Service Temp.(ºC)	1800
Compressive strength (Mpa)	≥3900
Bending strength(MPa)	400-580
Fracture strength(MPa)	3.05-4.6
Young's modulus(Gpa)	380-410
Thermal conductivity  W/MK	102.6
Thermal expansion a(1/ºC)	4.02x10
Poisson's ratio	0.14
Apparent porosity %	0